PRODUCTION DESCRIPTION
RCVD (Rotary Conical Vacuum Dryer)/CDB(Conical Dryer Blender) is a kind of multi-functional machine of mixing & vacuum drying, it is a batch type fully closed process equipment for solid-liquid separation, vacuum drying of powder & granular solid and low -temperature concentrating of reaction solution, which is widely used in chemical industry, fine chemical industry, foodstuffs industry and pharmaceutical process industry. The excellent corrosion resistance, anti-stick and cleanliness of the glass-lined vessel is especially suitable applicating for material that easy to be oxidized, volatilized, heat sensitive & toxic, not permitted to destroy its crystal in drying process, and the solution should tobe recovering.
Glass-lined RCVD/CDB is a fully closed pressure vessel equipment. Its constructure mainly includes a glass-lined double-conical vessel, a heating/cooling jacket, a frame, driving system, sealing device, vacuum system, rotary joint, temperature and pressure measurement device, control device and etc. |
 |
SPECIFICATIONS:
| Capacity: |
200 to 5000 Liters |
| Loading Capacity: |
50%±10% of rated capacity |
| Drying Intensity: |
2.0 to 3.0 K/m2h |
| Working/Designed Pressure: |
Vessel: -0.098/-0.098 ~ 0.4Mpa
Jacket: 0~0.3/0.4Mpa |
| Working/Designed Temperature: |
Vessel: 20 ~130ºC/143ºC Max.
Jacket: 20 ~150ºC/150ºC Max. |
| Working Medium: |
Vessel: Wet Material
Jacket: Hot water / Steam / Thermal Oil |
| Thickness of Lined Glass: |
0.8 to 2.0 mm |
| Swing Speed of Vessel: |
0.6~12rpm |
| Max. Leackage Rate of Gas: |
1330Pa·L/s |
| Driving Device: |
6 Pole Flameproof Motor+Warm Gear Reducer |
| Shaft Seal: |
PTFE Packing Type Seal + Rotary Joint |
| Standard/Design Code: |
HG/T 3682-2000 Or Against customized standard |
|
APPLICATIONS OF RCVD/CDB
| Suitable materials with powder and granular state: |
Heat-sensitive materials that should be drying at low temperature;
Oxygen-sensitive with hazardous materials;
Materials that requiring recovery of toxic solvents and gases;
Materials that required with low residual volatile content;
Materials that required mixed/blended sufficiently and evenly. |
| Inapplication materials and operating conditions: |
Hydrofluoric acid & media which containing fluoride ions with all concentration and temperature;
Phosphoric acid with concentration is over than 30% with temperature is higher than 180°C;
Alkaline which PH value more than 12 with temperature higher than 80°C;
When the temperature changes drastically during glass lined equipment working, the excessive thermal stress will cause the lined glass damage of the equipment. Therefore, the temperature should be raised or lowered slowly during equipment operating.
Materials that easy to agglomerate during drying process |
|
WORKING PRINCIPLE
| After the wet materials are feed into the vessel of RCVD/CDB, close all the valves and lips on the vessel and then start the vacuum pump; heating the vessel body by jacket pass though the heating media(hot water /steam/ thermal oil); the heat is in contact with the wet material through the inner wall of the vessel body,moisture is evaporated from the wet material, then the vapor is pumped out by the vacuum pump through the vacuum exhaust pipe; since the vessel is in a vacuum and rotating state to make the material constantly turn up and down inside and outside, so speed up the drying speed of the wet material, improve the drying efficiency, and achieve the purpose of uniform drying of the material. |
|
PRODUCTION PROCESS
FEATURES OF GLASS LINED EQUIPMENT
Corrosion Resistance - glass is extremely resistant to corrosion by acids and alkalies (except for hydrofluoric acid and hot concentrated phosphoric acid)
Anti-stick - many substances will not stick to glass, but will stick to metal
Purity - glass has high quality standards for food and drug applications
Flexibility - glass can handle a diverse range of chemical conditions
Easy To Clean - glass-lining surface enables quick, easy cleaning and sterilization
Absence Of Catalytic Effect - eliminates the possibility of catalytic effect that can occur in vessels made with various exotic metals
Economy - the cost is comparable to stainless steel and most alloys
Excellent Insulation - When does 10KV high-frequency spark testing, the electric spark can not penetrate the glass linings
Extremely Corrosion Resistance - According to the characteristics of working medium designing the material for extremely corrosion resistance
Temperature Resistance - Thermal conductivity is only 1 to 0.1 percent of metal
Impact Resistance - The impact resistance of superior products is 260*10-3J
Customized Design - Design and manufacture according to the condition and requirement of customer
PRODUCT ADVANTAGES
Vacuum Drying - Vacuum drying (VD) has some distinctive characteristics such as higher drying rate, lower drying temperature, and oxygen-deficient processing environment. It is conceptually the ideal method for drying heat and/or oxygen sensitive materials due to the advantage of removing moisture at low temperatures and minimizing the possibility of oxidation reactions. During vacuum drying, high-energy mloisture molecules diffuse to the surface and evaporate due to low pressure. Due to the absence of air and bacteria, vacuum drying prevents oxidation and maintains the color, texture, and flavor of the dried products.Vacuum-drying is proposed to alleviate some disadvantages of hot-air-drying, such as surface hardening and dispersion. During vacuum drying, the rate of evaporation increases (at a fixed temperature) since the boiling point of moisture is reduced. Vacuum-drying consequently requires less drying time than conventional hot-air-drying and in most cases results in a higher quality dried product.
Multifuctional - The glass lined RCVD/CDB performs a multitude of tasks including mixing/blending, vacuum drying, and recovery of solvents (should connected with condensing system) .
High Applicability - The rotating speed of vessel can be flexibly adjusted through the frequency conversion flameproof motor and controller to adapt to the changes in the specific gravity and viscosity of material, and improve the efficiency of drying process.
Configurability & Cleanliness - Pneumatic control feed/discharge valves, weighing system, CIP/MIP and SIP systems can be added to meet the requirements of GMP standard clean production and automatic control to reduce the cross contamination risk. |
|
EFFECTED FACTORS OF EQUIPMENT OPERATION
Material Characteristics:
Viscosity of material - The viscosity of the material changes with its moisture content. The viscosity can make the material agglomerate into blocks and adhere to the vessel inner wall. After drying, it is easy to adhere to the inner wall of dust collector and pipe.
Allowable temperature of material - The allowable temperature is the maximum temperature that the material can withstand. If the temperature is exceeded by heating, the potency of the material will change, material will decompose or change color.
Bulk density of materials - The mass per unit volume of material is called bulk density. Because the material is a mixture of dry material and moisture content, dry material is often in granular, powdery or solid block state, the gap between the particles of dry material is different with the different moisture content. The bulk density of wet material will be change from drying process, so pay attention to the selection of dryer.
Slip angle of material - The side materials will slide downward when the angle between the slope and the bottom increases to a certain angle during stacking granular or powdery state materials. This angle named slip angle of material, and related to material composition, moisture content, particle size and viscosity. The cone angle of RCVD/CDB should be refer to the slip angle of the material.
Heating Temperature & Drying Speed:
Heating temperature - It is necessary to select the appropriate temperature during drying according to the different characteristics of materials. Generally, the variable temperature drying method can be used. In the early stage of drying, the heating temperature is low, and then temperature is gradually increased to improve the drying rate.
Drying speed - At the beginning of RCVD/CDB vacuumizing and heating, the drying speed of material is slow; When the material temperature is heated above the boiling point of water/solvent, the drying speed will suddenly speed up. The moisture of material is heated into vapor state under the corresponding pressure within the allowable temperature range, and the heat added is used for vaporization heat and various heat losses, at this time the temperature of the material remains unchanged. The vacuum system continuously discharges vaporized steam to keep the pressure difference between the material evaporation surface and the space to makes the drying continue; When the moisture content of the material is reduced to a certain value, the moisture evaporated from the material is reduced, the temperature of the material begins to rise under the condition of constant heating capacity, the pressure difference between the material evaporation surface and the space decreases, and the drying speed turns into the deceleration stage and gradually decreased to zero.
Working Pressure of Vessel: Generally, the working pressure inner vessel of RCVD/CDB keeps -0.09 to -0.098Mpa; drying speed turns quickly during the vessel under low pressure,but too low will cause the cost of vacuum system increasing, and it is diseconomy.
Swing Speed of Vessel: Theoretically, the drying speed is more quickly with the vessel of RCVD/CDB rotates more faster. However, in the earlier of vacuum drying process, it is easy to cause the wet materials to agglomerate with faster rotation speed of vessel. Therefore, during the earlier of drying process, the rotation speed of the vessel can be increased after the material surface is dry. In the later of drying process, the rotation speed of vessel should be reduced appropriately with the decrease of moisture content, the increase of rotation speed has little effect on the increase of drying speed at this time. Therefore, during the drying process, the staff should adjust the rotation speed of the vessel according to the drying conditions of the materials at any time.
HOW TO AVOIDING DAMAGE IN GLASS LINED EQUIPMENTS
There are four main categories of failure modes that can occur in glass lined equipment: mechanical, thermal, electrical, and chemical. These issues, however, can be eliminated or drastically reduced through the identification of the various types of damage and by asserting the best practices to avoid them.
# Mechanical Category
- Mechanical Impact
Internal impact - Internal impact occurs when something hard hits the interior lining surface. When you are working in a reactor, it is important to pad the floor and mixer before entering the vessel to prevent an accidental internal impact to cracking the glass lined surface from a loose item or tool that is dropped.
External impact - While glass is quite strong in compression, it is weak in tension so a direct blow to the exterior of the vessel can cause a "spall" or star-shaped crack pattern to the interior glass lining. Avoiding a sudden external force to the glass lined reactor is an easy way to prevent this type of damage from occurring.
Hydro blasting - Installing a wash-in-place system via spray balls and other type of pressure equipment is an effective way to keep your vessel clean. However, if the high-pressure cleaning exceeds 137 bar (2000 psi) or if the water jet is less than 30cm (12 inches) from the vessel wall, damage can occur (there are situations where greater allowances are acceptable, but this is a general best practice). Additionally, abrasive particles mixed with the water can contribute to hydro blast damage as can water sprayed on a specific area for a prolonged period of time and direct contact to repairs such as patches or plugs.
Abrasion - When particles that are harder than the glass surface contact it, abrasion can occur. This often happens at the edges of nozzles, baffles and agitators due to vigorous mixing.
Cavitation - Caused by condensation, pressure decrease, and chemical reaction, cavitation is the damage that occurs when bubbles collapse at the glass surface. Incorporating Nitrogen into your process can help to subside bubble collapse and using a sparger is also a way to combat cavitation.
- Mechanical Stress
Crushing - Despite its compressible strength, improper flange makeup and uneven or over-torquing can crush glass. In addition to carefully selecting your gaskets and following proper flange assembly techniques, calibrated torque wrenches must be used to avoid excessive stresses.
Bending - When piping systems are not adequately installed and supported, the connection to the vessel is subject to excessive tensile and compressible forces which can lead to bending damage. Bending damage is evident from the cracks that appear at the bending axis.
Vibration - When baffles, dip pipes and other accessories that are installed via nozzles are not sized and positioned properly, it can result in vibrations that can cause glass damage so widespread that the only solution is re-coating glass. This can be prevented, however, by properly aligning your agitator and other internal components as well as being conscious of water hammer and using the right sparger device for steam injection.
# Thermal Category
- Thermal Shock
General thermal shock - Any time the glass lined reactor experience a sudden change in temperature that is in excess to the recommended limit, you are exposing your vessel to potential thermal shock. Adding hot liquid to a cold vessel wall or conversely cold liquid to a hot glass surface creates an environment of increased tensile stress on the lining.
Local thermal shock - This term refers to thermal shock damage that is localized, for example, injects steam that from a leaking valve on a particular area of the glass lined surface.
Welding near glass - One of the critical "don'ts" in glass lined equipment care is "don't weld components onto your equipment interior or exterior." Welding and glass surfaces are generally are not a good combination due to the risk of thermal shock; welding on glass lined equipment will almost always cause glass damage.
- Thermal Stress
Restricted flexibility from large fillet welds - Thermal shock is most prevalent at fillet welds between the vessel shell and jacket as well as at the top and bottom jacket closure rings. This is due to the high stress concentration in these areas. Additionally, any build-up of sludge in the reactor jacket and attribute to thermal stress risks. By blowing down the build-up on a regular basis, you can avoid plugging the outlet nozzle diaphragm ring which will decrease chances of thermal stress damage.
Expansion of steel - The steel substrate of a vessel can expand for a number of reasons, freezing of the interior contents and over-pressurization of the vessel being the two most common. This expansion results in a series of cracks to the lining. In the case of agitators and baffles, if liquid that accumulates inside the hollow centers freezes, the glass often falls off in long shards.
# Electrical Category
Electrostatic discharge - Static charges can build up for a number of reasons, including processes involving low-conductivity organic solvents, and operational practices such as introducing free-falling liquids and powders as well as excessive agitation. If the dielectric strength exceeds 500 V per mil of thickness, it can result in damage to the glass lining. The most affected parts of the vessel are generally located near high-velocity areas like the tips of agitator blades and the vessel wall opposite the blades. The damage usually appears as microscopic holes that go all the way down into the steel substrate; chipping may or may not occur. You can also usually see a discoloration, or "aura", around the pinhole. To avoid putting your vessel at risk, keep your agitation speeds at a minimum and add materials through dip tubes so that they enter below the liquid level line.
Spark testing - Spark testing is the most commonly-used method for inspecting glass lined equipment. The metal brush that is moved across the glass surface will generate a spark to indicate a defect in the lining. The most common problem faced with spark testing is that personnel use excessive voltages (levels that should only be used by glass manufacturers when they are running quality checks on new equipment) or linger in one area too long. We normally recommend 10 KV for field testing, and the brush should also be moving over the surface. Furthermore, spark testing should only be used occasionally. It is always recommended that a qualified technician performs spark testing in glass lined equipment. When the procedure is mishandled, it can create pinholes in the glass that will look similar to electrostatic discharge damage.
# Chemical Attach
- Glass lining
Minimum available glass thickness - While glass lining is well known for its exceptional corrosion resistance, you still need to take into account that it does corrode. The rate will normally be determined by the chemistry medium and temperatures involved in the process. Still, there is a diminishing of the glass thickness over time that needs to be taken into account and checked periodically. When glass thickness becomes excessively worn you may notice a number of symptoms like loss of fire polish, smoothness and even chipping and pinholes.
Corrosion by water - The alkaline ions that are found in distilled, hot water can actually leach onto the glass surface when they are in the vapor phase and lead to a roughening of the glass surface and possibly chipping. You may also find vertical ridges if the damage is caused by condensate running down the wall. The preventative solution is to clean the vessel with water that includes a small amount of acid.
Corrosion by acids - While glass provides excellent resistance to most acids, there are three types which cause significant damage - hydrofluoric acid, phosphoric acid, and phosphorus acids. When glass is attacked by these acids, especially when they are concentrated solutions, corrosion can occur quickly. Temperature also plays a key role in speeding up the contamination process.
Corrosion by alkalis - Hot and caustic alkalis should be avoided in glass lined equipment. Silica, the main component of glass is very soluble in alkali solutions, making chemicals such as sodium hydroxide and potassium hydroxide a hazard to your equipment. Visual signs that your equipment has been corroded by alkalis include a dull, rough finish, pinholes, and chipping.
Corrosion by salts - Salts corroding glass is based on the formation of acidic ions that attack the glass. The level of damage depends on the type of ion that forms. Acidic fluorides tend to be the most damage inducing. The best preventative measure is to anticipate the negative effects of these acid ions such as chlorides, lithium, magnesium and aluminum. When damage is caused from the liquid phase, there is a significant loss in fire polish and a roughening of the surface; in the vapor phase the attack is more concentrated to a specific area.
- Repair Materials
Degradation of tantalum patches and plugs - Tantalum is a commonly used repair material for glass because it has very similar corrosion resistance. There are, however, a few exceptions in which tantalum corrodes at a greater rate. In these instances, the tantalum may embrittle when hydrogen is the byproduct of a corrosive reaction. By avoiding galvanic couples, you can help deter this from happening. Regular inspection of all patches and plugs should also be performed to check for signs of embrittlement (these signs being missing pieces or cracks in the tantalum). Sometimes a small amount of platinum is applied to the plug to prevent embrittlement. In addition to cracking, glass fracture around the repair area and a rust-colored stain are also signs of damage. A damaged plug should be replaced, but if the same issue repeats itself, the solution is to come up with an alternative metal that can be substituted for the tantalum.
Attack of furan cements - There are certain process environments that can attack furan cement. Strong oxidizers and sulfuric acid solutions and some moderately strong acids are typical culprits. There is often no visible sign that the cement has been affected. If you notice a gap between your repair plug and the glass surface, though, this is an indication that the cement has been compromised. In this instance, the repair should be redone and a different type of cement should be selected.
Attack of silicate cements - Silicate cements, on the other hand, tend to be vulnerable to water or steam (when they are not completely cured), alkalis and hydrofluoric acid. As with other types of cements, the only indication of attack is usually a gap found in between the repair plug and glass surface and the solution is to repair the damaged area using another type of cement that is more compliant with your process.
Damage to PTFE components - PTFE is a common material used in nozzle liners, agitator blade "boots", repair gaskets, and other components. Acetic acid, polymerizations (e.g. PVC), and bromine are all examples of compounds that can permeate and degrade PTFE. Additionally, PTFE has a temperature limitation of 260 ºC(500°F )and can develop HF vapors at higher temperatures that…well, we all know by now what hydrofluoric acid can do to glass! When PTFE is damaged it is apparent from the cracked, torn, and/or blistered appearance exhibited by the otherwise smooth surface. If your operation requirements don't match the limitations of PTFE, the material needs to be replaced with a different polymer or a modified PTFE that can withstand more extreme applications.
- Steel
Corrosion from external spills or wet insulation - The steel corrosion can be caused by an external spill. Due to the popularity of chemicals entering from a top head nozzle and existing from a bottom head nozzle, these are common areas where fluid can be inadvertently spilled or leaked. This type of incident is particularly damaging to the vessel because the external spill/leak generate hydrogen atoms that diffuse through the steel all the way to the glass/steel interface. There they form hydrogen molecules and build-up until the bond between the glass and steel are disrupted. This damage, known as "spalling" is usually too large for a patch or plug and therefore requires re-coating glass.
Damage from chemical cleaning of jacket - Jacket care and cleaning is an important topic that critical to keeping your reactor running efficiently. Eventually, heating or cooling media accumulates and leaves unwanted deposits in your jacket, making it necessary to clean it out. When the incorrect cleaning solutions are used, such as hydrochloric acid or other acid solutions, this can have a devastating impact on your reactor, similar to the spalling we just described. To avoid this, be sure to use dilute sodium hypochlorite solution or another neutral cleaner. Damage of this kind will take on the fish scale appearance.
Flange face spalling - One of the most common types of damage found in glass lined equipment comes from corrosive chemicals that escape from flange connections. This "edge-chipping" as it can be know, is caused by chemicals that leak through the gasket and attack the outside edge around the flange, causing glass to flake away on the gasket surface and ruining the sealing surface. Flange face spalling is corrected through the use of an outside metal sleeve, outside PTFE sleeve or epoxy putty.
CONTACT
SHANDONG PIONEER HEAVY INDUSTRY TECHNOLOGY CO.,LTD.
Tel/Fax: 0086 533 3171219
Address : Changwang Industrial Park, Liushan Town, Linqu County, Weifang City, Shandong Province, P.R.China
Miss Coco LEE
Mobile: 0086 13581033322
Mr. Conan WEI
Mobile: 0086 18653336026
){kind=link}
){kind=link}